Abstract
MDF (Medium Density Fiberboard) and WPC (Wood Plastic Composite) are innovative results of using sawdust waste to overcome the problem of wood scarcity. This study used a WPC Teak dowel because it has high shear strength and does not cause rust marks. This study was conducted to determine the value of the MDF connection capacity using WPC Teak dowel connectors and to determine the connection failure mode based on the EYM (European Yield Model) theory. This study used a WPC Teak dowel with a diameter of 6 mm, 8 mm, 10 mm, and 12 mm. The type of connection is a double-shear wooden joint using MDF. The test was carried out at the Structural Laboratory, Civil Engineering Department, Tidar University using a Compression Testing Machine to get the value of the connection capacity and test failure mode based on the MDF bearing strength and WPC Teak post failure referring to ASTM D764-97a. The test results obtained an average connection capacity value WPC dowel with a diameter of 6 mm, 8 mm, 10 mm, and 12 mm, respectively, which was 1094 N; 1870 N; 2439 N; and 3462. The highest average connection capacity value at 12 mm diameter was 3462 N, and the lowest at 6 mm was 1094 N.
Keywords
Article Details
References
- Arnandha, Y., Satyarno, I., Awaludin, A., Fardhani, A., 2016, Evaluasi Kuat Tumpu Alat Sambung Baut pada Papan WPC dari Limbah Sengon dan Plastik HDPE, Jurnal Media Komunikasi Teknik Sipil, Vol 22, No.2, Yogyakarta.
- Aruan, I., C., A., 2019, Analisa Variasi Kecepatan Putar Spindel dan Kecepatan Pemakanan terhadap Kehalusan Permukaan Kayu MDF pada Mesin Mini Router CNC Tiga Axis, Skripsi, Universitas Bangka Belitung, Bangka Belitung.
- Ayubi, K., A., A., 2020, Studi Penggunaan Baut pada Wood Plastic Composite (WPC) Jati dengan Metode Geser Dua Irisan, Skripsi, Universitas Tidar, Magelang.
- Ismayadi, A., 2018, Kapasitas Sambungan Kayu Tampang Dua dengan Variasi Sudut Memakai Alat Sambung Pasak Bambu Dilapisi Perekat, Skripsi, Universitas Mataram, Mataram.
- National Design Specification for Wood Contruction (NDS) 2018 National Design Specification, Edition, Leesburg: America Wood Council.
- Putra, G., W., A., 2014, Pemanfaatan Rumput Laut sebagai Alternatif Pengganti Serbuk Kayu untuk pembuatan Medium Density Fibreboard (MDF), Skripsi, Universitas Airlangga, Surabaya.
- Spesifikasi Desain untuk Konstruksi Kayu, 2013, SNI 7973:2013, Badan Standardisasi Nasional, Jakarta.
- Standard Test Method for Evaluating Dowel-Bearing Strength of Wood and Wood-Based Products, 2002, ASTM D5764-97a, Volume 04. 10 Wood ASTM, West Conshohocken, PA: ASTM International.
- Sulistyo, D., F., 2018, Pengujian Kuat Sambungan Bambu Laminasi dengan Metode Sambungan Geser Satu Irisan Menggunakan Alat Sambung Baut, Skripsi, Universitas Islam Indonesia, Yogyakarta.
- Tanubrata, M., 2015, Bahan-bahan Konstruksi dalam Konteks Teknik Sipil, Jurnal Teknik Sipil Vol 11 No. 2, Universitas Kristen Maranatha, Bandung.
- Vachlepi, A., 2015, Produksi Medium Density Fiberboard (MDF) dari Kayu Karet di Sumatera Selatan : Potensi, Mutu dan Proses Pengolahannya, Warta Perkaretan, 34 (2), 177-186.
- Sudrajad, I., 2020, Uji Kekuatan Papan Wood Plastic Composite (WPC) Limbah Serbuk Kayu Jati Dan Limbah Plastik High Density Polyethylene (HDPE) Sebagai Persyaratan Struktur, Tugas Akhir Program Studi Teknik Sipil Universitas Islam Indonesia, Yogyakarta
- Vachlepi, A. 2015, Produksi Medium Density Fibreboard (Mdf) Dari Kayu Karet Di Sumatera Selatan : Potensi, Mutu Dan Proses Pengolahannya, Warta Perkaretan 2015, 34 (2), 177-186.
- Wijanarko, F., B., 2016, Studi Penggunaan Baut pada Wood Plastic Composite (WPC) dengan Metode Geser Dua Irisan (Double Shear Connections), Skripsi, Universitas Gadjah Mada, Yogyakarta.
References
Arnandha, Y., Satyarno, I., Awaludin, A., Fardhani, A., 2016, Evaluasi Kuat Tumpu Alat Sambung Baut pada Papan WPC dari Limbah Sengon dan Plastik HDPE, Jurnal Media Komunikasi Teknik Sipil, Vol 22, No.2, Yogyakarta.
Aruan, I., C., A., 2019, Analisa Variasi Kecepatan Putar Spindel dan Kecepatan Pemakanan terhadap Kehalusan Permukaan Kayu MDF pada Mesin Mini Router CNC Tiga Axis, Skripsi, Universitas Bangka Belitung, Bangka Belitung.
Ayubi, K., A., A., 2020, Studi Penggunaan Baut pada Wood Plastic Composite (WPC) Jati dengan Metode Geser Dua Irisan, Skripsi, Universitas Tidar, Magelang.
Ismayadi, A., 2018, Kapasitas Sambungan Kayu Tampang Dua dengan Variasi Sudut Memakai Alat Sambung Pasak Bambu Dilapisi Perekat, Skripsi, Universitas Mataram, Mataram.
National Design Specification for Wood Contruction (NDS) 2018 National Design Specification, Edition, Leesburg: America Wood Council.
Putra, G., W., A., 2014, Pemanfaatan Rumput Laut sebagai Alternatif Pengganti Serbuk Kayu untuk pembuatan Medium Density Fibreboard (MDF), Skripsi, Universitas Airlangga, Surabaya.
Spesifikasi Desain untuk Konstruksi Kayu, 2013, SNI 7973:2013, Badan Standardisasi Nasional, Jakarta.
Standard Test Method for Evaluating Dowel-Bearing Strength of Wood and Wood-Based Products, 2002, ASTM D5764-97a, Volume 04. 10 Wood ASTM, West Conshohocken, PA: ASTM International.
Sulistyo, D., F., 2018, Pengujian Kuat Sambungan Bambu Laminasi dengan Metode Sambungan Geser Satu Irisan Menggunakan Alat Sambung Baut, Skripsi, Universitas Islam Indonesia, Yogyakarta.
Tanubrata, M., 2015, Bahan-bahan Konstruksi dalam Konteks Teknik Sipil, Jurnal Teknik Sipil Vol 11 No. 2, Universitas Kristen Maranatha, Bandung.
Vachlepi, A., 2015, Produksi Medium Density Fiberboard (MDF) dari Kayu Karet di Sumatera Selatan : Potensi, Mutu dan Proses Pengolahannya, Warta Perkaretan, 34 (2), 177-186.
Sudrajad, I., 2020, Uji Kekuatan Papan Wood Plastic Composite (WPC) Limbah Serbuk Kayu Jati Dan Limbah Plastik High Density Polyethylene (HDPE) Sebagai Persyaratan Struktur, Tugas Akhir Program Studi Teknik Sipil Universitas Islam Indonesia, Yogyakarta
Vachlepi, A. 2015, Produksi Medium Density Fibreboard (Mdf) Dari Kayu Karet Di Sumatera Selatan : Potensi, Mutu Dan Proses Pengolahannya, Warta Perkaretan 2015, 34 (2), 177-186.
Wijanarko, F., B., 2016, Studi Penggunaan Baut pada Wood Plastic Composite (WPC) dengan Metode Geser Dua Irisan (Double Shear Connections), Skripsi, Universitas Gadjah Mada, Yogyakarta.